Cuttlebone Cast Silver Pendant



I mentioned a while ago that I'd been doing some cuttlebone casting at my jewellery night class and that I would post about it. Well this is the pendant I made from the cast silver. You wouldn't know it was cast from a cuttlefish bone really but I did learn several things by making it including what not to do when tube setting!

I took some scrap silver in to college to use for the casting rather than pay for casting grains and made my mould in the cuttlebone. I went for a simple rectangle shape just to keep it simple rather than try to create a more intricate design that possibly wouldn't work. My first mistake was to use all the scrap silver I'd taken in - all 35g of it! It took forever to melt in the crucible and at one point there were two of us with two torches going at it. I actually gave up at one point then realized that the silver was stuck in the crucible so I'd have to carry on and get it flowing. Eventually (after about 20 mins) the silver scrap started to melt and it could be poured into the cuttlebone mould. Part of the cuttlebone snapped off at the bottom as it was too thin but I did end up with this....


 It was thicker than I hoped but what a lovely texture! I wanted to thin it down a bit as I was hoping to sell whatever I made and didn't want it to be over 7.78g otherwise I would need to get it hallmarked so I took the thing with the beautiful texture and flattened it in the rolling mill!

I then cut a shield shape out of it and added a partial heart cut out at the side. I soldered on a bail and a silver ball. The silver ball took three attempts - the first time I soldered it to the back of the bail by mistake, the second there wasn't enough solder and it came off so I did it again at home. I usually need to sort out things at home as soldering in class always seems to go wrong for some reason.
In the meantime we were shown how to tube set so I thought I'd add a tube set faceted gemstone to the pendant. My first attempt didn't go too well. I forgot about the culet (the pointy bit at the bottom of the gemstone) and cut my tube too short! So when I set it the culet touched the pendant and the gemstone skewed over to the side slightly. I also used a setting punch which was too big and left a lovely ring stamped around the base of the tube on the pendant. I'd been so engrossed in looking at the gemstone when I was setting it I didn't even notice the stamped ring. So after swearing quite a bit and sanding out the stamped ring this is what it looked like after I'd oxidized it.....



You can see in this photo how the gemstone isn't level. I finished it but wasn't really happy but when I took it into class everyone said it looked ok and you couldn't see it wasn't completely level. I was sort of reassured but as I wanted to sell it and knowing it wasn't "right" I decided to sort it out and start again. So here it is with the stone and tube setting removed, cleaned up and new tube setting soldered on...





Putting it through the rolling mill did flatten the texture a lot but it still has some texture plus I was able to sand the bottom part smoother making it easier to solder the tube setting onto it. I finished it by setting a stabilized turquoise cab into the tube setting and oxidizing it.


I was quite glad to see it finished to be honest! I seemed to spend weeks working on it. I listed it in my Etsy shop and it sold earlier this week and is now on it's way to California. 

Goodbye my first cast and tube set pendant, you drove me completely nuts but thank you for teaching me what not to do :D


Comments

  1. Fantastic job!! I would love to have a go at casting one day. So happy you were able to rework the piece to how you wanted it, it's really satisfying when you can do that :)

    ReplyDelete
  2. Thanks, I was glad I could sort it out too!

    ReplyDelete

Post a Comment

Your comments and questions are very welcome!
If you would prefer to contact me directly please use the contact form on my "get in touch" page.

Popular posts from this blog

Combining Soldering And Enamel

The need to make cute, brightly coloured enamel studs propelled me into the world of combining soldering with enamel a couple of years ago. I knew from reading up on it that it was possible to enamel and solder on the same piece but wasn't too confident I was able to do it back then. It was a slightly embarrassing occurance that made me just get on with - I'd made some enamel studs with glued on stud posts. I'd used 2 part epoxy resin which was a job in itself as it set hard after 5 minutes so I had to keep mixing more up. The finished studs looked ok but that little voice in my head kept asking "are you sure you want to use glue?" I wasn't but didn't think I had any other way to do it so I used glue. I sold my first pair and merrily sent them on their way to Canada. A couple of week later the buyer got in touch to say the stud post had come off one of the earrings and the other was hanging off. I was mortified, apologized profusely and refunded her m

Etching Silver Using Nail Art Stamps

So my love/hate relationship with etching sterling silver continues. I've tried a few times now and always end up with different results most of them not that great to be honest. I've tried connecting the silver and a piece of copper to a 9v battery and also heating the ferric nitrate. Sometimes the results are good sometimes not so good. I currently have an etched piece of silver sheet waiting to be reticulated and rid it of the mess that is the etched "pattern".  I now know that using stamps and Stayz On ink just doesn't work with silver - the time needed to etch using ferric nitrate is much longer than etching copper and the ink starts to wear away after about an hour. This results in the pattern being patchy as the resist is eaten away and the silver ends up quite lumpy and course looking. I have yet to try using pnp paper. I don't know why but it all seems a bit of a faff to do. I don't have a laser printer so would need to find somewhere or

Embossing Metal With My Sizzix Bigshot

I must admit up until a few weeks ago I was vaguely familiar with the name Sizzix but as to what you actually did with a "Sizzix" I was completely in the dark! That was until I stumbled across a video from Vintaj showing how you could use their embossing folders with a Bigshot to create designs on metal ("metal" - my favourite word after chocolate!) I was really impressed and itching to have a go, I just needed a Bigshot........ I waited a few weeks then when the urge to possess one overcame me I went out debit card at the ready..............and the shop had sold out! So I trundled off to The Range on the off chance and came home clutching my own surprisingly heavy pink and black wonder machine. It sat on the dining room table for a couple of days while I waited for the embossing folders I'd ordered online to arrive then the time came to start playing! I started with some pre-cut 24g copper hearts and the Wildflower Vines and the Butterfly Swirls Deco